High performance ceramics 3 d printers, based on the curing light special ceramic paste 3d printing materials (ceramic materials for 3 d printing alumina (AI2O3) m zirconia (ZRO2), hydroxyapatite (HAP), tricalcium phosphate (TCP), etc.) of ceramic 3 d printing, use CAD data directly, without mould, allow the diversity of product design,The design can be changed in the computer at any time, the mechanism and shape are not restricted by any restrictions (bottom cut, honeycomb structure and inner cavity), excellent surface quality, fast and economical production of high-performance ceramic functional parts, material properties are not lower than the traditional mode (pressing or injection molding, etc.) mass production parts.Widely used in industry, aerospace, jewelry, luxury accessories, medical implants.
Ceramic 3D printing technical parameters
1, Ceramic 3D printer maximum molding printing size: 76x43x105mm;
2, 3D printing layer thickness: 25um~100 m;
3. Plane resolution: 40um (365dpi);
4, Pixel (X, Y) : 1920X1080;
5, light source: LED and laser;
Process flow of ceramic 3D printing
1. Design 3D model CAD data and convert the design document into.The STL format;
2. The 3D printing engineer set computer parameters and printer parameters;
3. Input the set parameters into the printer to print the product layer by layer until all the models are completed;
4. Take out the sample, clean it, and put it into the degreasing and sintering curing furnace;
5. If necessary, carry out post-processing of the surface;
3D printed material data
| Material | zirconia-ZrO2 |
| 4P- Bending strength | 650MPa |
| The purity | ＞6.01g/㎝³(99.4%T.D..) |
| Surface roughness（Ra） | ~0.6µm |
| Material | High purity alumina-Al2O3 |
| 4P- Bending strength | 430MPa |
| The purity | ＞3.96g/㎝³(99.4%T.D..) |
| Surface roughness（Ra） | ~0.4µm |
According to customer needs, we can develop special materials, such as ATZ, HAP, TCP tricalcium carbonate glass ceramics, oxides, nitrides and carbides.