Describe
SLA white resin 3D printing service is mainly for parts with high requirements on appearance. After forming, the surface is exquisite, the detail expression is very good, the precision is high, and the price is cheap, which is the most cost-effective material at present.
However, the material strength is not high, and the temperature resistance is not good, and oxidation may occur easily after a long time, so it can only be used as a sample for a short period of time, and the effect may not be good for a long time.
Post-treatment process：We provide paint painting, screen printing, electroplating and other post-processing services.
Process
Introduction to material properties
Material Color：White
Tolerance：±0.1mm
Temperature Resistance：40℃-60℃
Minimum Wall Thickness：0.8mm
The surface is relatively smooth, suitable for painting, silk screen, electroplating and other finish post-processes.
The material is relatively crisp (approximately similar to the strength of the transparent ruler we usually use), and is often used for display, exhibition, exposure, proofing and other aspects.
Material parameters
| Hot deformation temperature | 46℃ |
| Hardness | 79 |
| Tensile strength (tensile) | 47MPa |
| Tensile strength (fracture) | 33-40MPa |
| Extension rate (tensile) | 3% |
| Extension rate (fracture) | 6%-9% |
| Elastic modulus | 2370-2650MPa |
| Bending strength | 67MPa |
| Bending modulus | 2178-2222MPa |
| Impact strength | 23-29J/M² |
| Water absorption | 0.40% |
| Poisson’s ratio | 0.41 |
Product Display